Experimental Study on Post-Buckled Composite Single-Stringer Specimens with Initial Delamination under Fatigue Loads

ANTONIO RAIMONDO, JAVIER PAZ MENDEZ, CHIARA BISAGNI

Abstract


The fatigue damage tolerance of a composite stiffened structure in post-buckling conditions is experimentally investigated in this work. Single-stringer specimens with an initial delamination, artificially created during the manufacturing process, are tested under cyclic compressive load. Six nominally identical specimens are manufactured: two tested under quasi-static load to understand the compressive behavior of the structure and four under fatigue load cycling between pre- and post-buckling conditions at two different maximum loads. During the tests, digital image correlation system and ultrasonic C-scan are adopted to follow the evolution of the out-of-plane displacements and the propagation of the delamination. Depending on the load level, the delamination starts to grow already in the first cycle or after a few thousand cycles, but in both cases the propagation is fast at the beginning, then slows down gradually. The fatigue tests are interrupted after 150,000 cycles and the specimens are subjected to quasi-static compressive load to evaluate the residual strength of the structure.


DOI
10.12783/asc36/35772

Full Text:

PDF

References


Bisagni, C., R. Vescovini, and C.G. Dávila. 2011. “Development of a Single-stringer Compression

Specimen for the Assessment of Damage Tolerance of Postbuckled Structures,” Journal of Aircraft,

(2):495–502.

Anyfantis, K.N., N.G. Tsouvalis. 2012. “Post Buckling Progressive Failure Analysis of Composite

Laminated Stiffened Panels,” Applied Composite Materials, 19(3-4):219-236.

Turon, A., J. Costa, P.P. Camanho and C.G. Dávila. 2007. “Simulation of Delamination in

Composites Under High-cycle Fatigue,” Composites Part A: Applied Science and Manufacturing,

(11):2270-2282.

Raimondo A., and C Bisagni. 2019. “Analysis of Local Stress Ratio for Delamination in

Composites Under Fatigue Loads,” AIAA Journal, 58(1).

Raimondo, A., and C. Bisagni. 2020. “Fatigue Analysis of a Post-buckled Composite Singlestringer

Specimen Taking into Account the Local Stress Ratio,” Composite Part B: Engineering,

Dávila C.G. 2020. “From S-N to the Paris Law with a New Mixed-mode Cohesive Fatigue Model

for Delamination in Composites,” Theoretical and Applied Fracture Mechanics, 106.

Agarwal, B.L. 1982. “Postbuckling Behavior of Composite-stiffened-curved Panels Loaded in

Compression—an Experimental Evaluation of Static and Fatigue Behavior of Graphite/Epoxy

Curved Hat-stiffened Compression Panels Loaded Well Beyond Initial Buckling,” Exp. Mech.,

(6):231–6.

Abramovich H., and T. Weller. 2012. “Repeated Buckling and Postbucking Behavior of Laminated

Stringer Stiffened Composite Panels With and Without Damage,” Int. J. Struct. Stab. Dyn., 4:807–

Cordisco P., and C. Bisagni. 2011. “Cyclic Buckling Tests Under Combined Loading on Pre-

Damaged Composite Stiffened Boxes,” AIAA Journal, 49(8):1795–1807.

Bisagni C., and C.G. Dávila. 2014. “Experimental Investigation of the Postbuckling Response and

Collapse of a Single-Stringer Specimen,” Composite Structures, 108:493-503.

Davila C.G., and C. Bisagni. 2018. “Fatigue Life and Damage Tolerance of Postbuckled Composite

Stiffened Structures with Indentation Damage,” Journal of Composite Materials, 52(7):931–943.

Dávila C.G., and C. Bisagni. 2017. “Fatigue Life and Damage Tolerance of Postbuckled Composite

Stiffened Structures with Initial Delamination,” Composite Structures, 131:73-84.


Refbacks

  • There are currently no refbacks.